Fabrication and properties of pressure-sintered reaction-bonded Si3N4 ceramics with addition of Eu2O3–MgO–Y2O3

Dense pressure-sintered reaction-bonded Si₃N₄ (PSRBSN) ceramics were obtained by a hot-press sintering method. Precursor Si powders were prepared with Eu₂O₃–MgO–Y₂O₃ sintering additive. The addition of Eu₂O₃–MgO–Y₂O₃ was shown to promote full nitridation of the Si powder. The nitrided Si₃N₄ particles had an equiaxial morphology, without whisker formation, after the Si powders doped with Eu₂O₃–MgO–Y₂O₃ were nitrided at 1400 °C for 2 h. After hot pressing, the relative density, Vickers hardness, flexural strength, and fracture toughness of the PSRBSN ceramics, with 5 wt% Eu₂O₃ doping, were 98.3 ± 0.2%, 17.8 ± 0.8 GPa, 697.0 ± 67.0 MPa, and 7.3 ± 0.3 MPa m^1/2, respectively. The thermal conductivity was 73.6 ± 0.2 W m^?1 K^?1, significantly higher than the counterpart without Eu₂O₃ doping, or with ZrO₂ doping by conventional methods.     

Synergistic Effects of Polybenzimidazole and Aramide on Enhancing Flame-Retardancy and Solubility

Aromatic and functional polymers with processibility derived from biobased starting materials are prerequisite considering sustainable society. Poly(2,5-benzimidazole)s are rigid-rod polymers to show ultrahigh thermal stability such as flame retardance, while usually suffer from poor solubility. Here, poly(benzimidazole-co-amide)s are synthesized from two biobased monomers, 3,4-diaminobenzoic acid and a semirigid comonomer, 4-aminohydrocinnamic acid. The copolymers with an amide composition of 80 mol% and higher are soluble in widely used polar solvents to fabricate the films keeping high flame retardance, which is comparable with popular high-performance polymers such as aromatic polyimides, polyetheretherketone, polyphenylene sulfide, etc.     

Agronomic performance of high oleic,low linolenic soybean in Tennessee

Soybean oil hydrogenation alters the linolenic acid molecule to prevent the oil from becoming rancid, however, health reports have indicated trans-fat caused by hydrogenation, is not generally regarded as safe. Typical soybeans contain approximately 80 g kg⁻¹ to 120 g kg⁻¹ linolenic acid and 240 g kg⁻¹ of oleic acid. In an effort to accommodate the need for high-quality oil, the United Soybean Board introduced an industry standard for a high oleic acid greater than 750 g kg⁻¹ and linolenic acid less than 30 g kg⁻¹ oil. By combing mutations in the soybean plant at four loci, FAD2-1A and FAD2-1B, oleate desaturase genes and FAD3A and FAD3C, linoleate desaturase genes, and seed oil will not require hydrogenation to prevent oxidation and produce high-quality oil. In 2017 and 2018, a study comparing four near-isogenic lines across multiple Tennessee locations was performed to identify agronomic traits associated with mutations in FAD3A and FAD3C loci, while holding FAD2-1A and FAD2-1B constant in the mutant (high oleic) state. Soybean lines were assessed for yield and oil quality based on mutations at FAD2-1 and FAD3 loci. Variations of wild-type and mutant genotypes were compared at FAD3A and FAD3C loci. Analysis using a generalized linear mixed model in SAS 9.4, indicated no yield drag or other negative agronomic traits associated with the high oleic and low linolenic acid genotype. All four mutations of fad2-1A, fad2-1B, fad3A, and fad3C were determined as necessary to produce a soybean with the new industry standard (>750 g kg⁻¹ oleic and <30 g kg⁻¹ linolenic acid) in a maturity group-IV-Late cultivar for Tennessee growers.     

高分子材料导热性能影响因素研究进展

介绍了高分子材料导热性能影响因素研究进展，重点阐释了聚合物基体的结构特性（链结构、分子间相互作用、取向、结晶度等）、导热填料（种类、含量、形态、尺寸等）以及制备方法等对高分子材料导热性能的影响。     

Spectroscopic properties and thermally stable orange-red luminescence of Sm:Zr:LiNbO3 and Sm:Hf:LiNbO3 for white LED applications

LiNbO₃ crystals activated by Sm³⁺ and co-doped with Zr⁴⁺ (Sm:Zr:LN) or Hf⁴⁺ (Sm:Hf:LN) were prepared by the Czochralski method. Detailed investigation on spectroscopic properties was conducted on the frame of Judd-Ofelt (J-O) theory. The J-O intensity parameters Ω_i (i = 2, 4, 6), fluorescence branching ratios and radiative lifetime of excited level ⁴G_5/2 were determined. Furthermore, the thermal stability of the strong orange-red emissions obtained under near-UV excitation in both crystals was evaluated. As high as 100% and 97% of integrated intensities at room temperature in Sm:Zr:LN and Sm:Hf:LN respectively were retained at 423 K, demonstrating the suppressed thermal attenuation. The temperature sensing performance based on fluorescence intensity ratio strategy was degraded at higher temperatures with relatively low sensitivities, while the shift of CIE chromaticity coordinates of Sm:Zr:LN and Sm:Hf:LN in the orange-red region was insignificant, demonstrating the color constancy with increasing temperature. With the efficient and thermally stable orange-red luminescence, Sm:Zr:LN and Sm:Hf:LN could serve as promising candidate materials for near-UV excited white light-emitting diodes.     

Thermal depolarization and electromechanical hardening in Zn2+-doped Na1/2Bi1/2TiO3-BaTiO3

Na_1/2Bi_1/2TiO₃-based materials have been earmarked for one of the first large-volume applications of lead-free piezoceramics in high-power ultrasonics. Zn²⁺-doping is demonstrated as a viable route to enhance the thermal depolarization temperature and electromechanically harden (1-y)Na_1/2Bi_1/2TiO₃-yBaTiO₃ (NBT100yBT) with a maximum achievable operating temperature of 150 °C and mechanical quality factor of 627 for 1 mole % Zn²⁺-doped NBT6BT. Although quenching from sintering temperatures has been recently touted to enhance T_F-R, with quenching the doped compositions featuring an additional increase in T_F-R by 17 °C, it exhibits negligible effect on the electromechanical properties. The effect is rationalized considering the missing influence on conductivity and therefore, negligible changes in the defect chemistry upon quenching. High-resolution diffraction indicates that Zn²⁺-doped samples favor the tetragonal phase with enhanced lattice distortion, further corroborated by ²³Na Nuclear Magnetic Resonance investigations.     

珠江口盆地珠一坳陷古近系高自然伽马砂岩形成机制及油气地质意义

运用放射性元素寻找油气是一种非常规油气勘探手段。近年来,在珠江口盆地珠一坳陷富烃凹陷周边古近系钻遇高自然伽马(GR)砂岩,其GR值(100~300 API)甚至大于同区泥岩的GR值(100~200 API)。为了弄清该特殊现象背后的地质意义,对珠江口盆地珠一坳陷古近系高自然伽马砂岩开展了铀(U)、钍(Th)、钾(K)等3种元素含量与GR值的相关趋势线分析,从井震特征、岩性特征及矿物成分特征等入手分析了砂岩GR值增高的主要原因及成因机制,探讨了放射性元素聚集的条件、运移通道、驱动力以及油气意义。结果表明:西江、惠州地区由U含量增高导致砂岩GR值偏高,恩平、番禺地区由K,Th含量增高导致砂岩GR值偏高;砂岩GR值增高有两大成因机制,一是地下流体带来的放射性元素离子U4+在氧化-还原面处富集后导致地层GR值偏高,这种特殊现象说明在具有连通基底大断裂旁的圈闭中,U4+的富集指示了曾经油气的存在,证实了研究区油气运移通道的有效性,对于油气藏的预测有着非常重要的指导性意义,二是地表流体带来的含放射性元素的矿物大量沉积后导致地层GR值偏高,含放射性元素矿物性质不稳定,可指示近源供给的存在,对于判断物源及沉积环境有着非常重要的意义。该研究成果为预测研究区油气成藏有利区带提供了依据。     

Microstructural and mechanical properties assessment of transient liquid phase bonding of CoCuFeMnNi high entropy alloy

The transient liquid phase (TLP) bonding of CoCuFeMnNi high entropy alloy (HEA) was studied. The TLP bonding was performed using AWS BNi-2 interlayer at 1050 °C with the TLP bonding time of 20, 60, 180 and 240 min. The effect of bonding time on the joint microstructure was characterized by SEM and EDS. Microstructural results confirmed that complete isothermal solidification occurred approximately at 240 min of bonding time. For samples bonded at 20, 60 and 180 min, athermal solidification zone was formed in the bonding area which included Cr-rich boride and Mn₃Si intermetallic compound. For all samples, the γ solid solution was formed in the isothermal solidification zone of the bonding zone. To evaluate the effect of TLP bonding time on mechanical properties of joints, the shear strength and micro-hardness of joints were measured. The results indicated a decrement of micro-hardness in the bonding zone and an increment of micro-hardness in the adjacent zone of joints. The minimum and maximum values of shear strength were 100 and 180 MPa for joints with the bonding time of 20 and 240 min, respectively.     

Low/intermediate temperature pyrolyzed polysiloxane derived ceramics with increased carbon for electrical applications

This study focuses on the chemistry, thermal stability, and electrical conductivity of low/intermediate pyrolysis temperature (700?900 °C) polysiloxane derived ceramics. These ceramics were modified with additional carbon derived from divinylbenzene (DVB) added to the precursor. Their electrical properties were investigated for potential uses in micro-electrical mechanical systems (MEMS) and anodes for lithium batteries. The microstructure and chemical composition was investigated by attenuated total reflectance Fourier transform infrared spectroscopy (ATR-FTIR), Raman spectroscopy, and x-ray photoelectron spectroscopy (XPS); thermogravimetric analysis (TGA) provided insight into the thermal stability; and electrochemical impedance spectroscopy (EIS) into the electrical properties of the material. The increase of pyrolysis temperature and carbon content lead to an enhancement of the electrical conductivity, higher than previously reported values for intermediate pyrolysis temperature SiOC polymer derived ceramics. A limit of the amount of DVB that can be added to PHMS to produce a hybrid precursor has also been obtained.     

Thermal transport and chemical conversion in single reacting sorbent particles

The effects of particle size and carbon dioxide concentration on chemical conversion in engineered spherical particles undergoing calcium oxide looping are investigated. Particles are thermochemically cycled in a furnace under different carbon dioxide concentrations. Changes in composition due to chemical reactions are measured using thermogravimetric analysis. Gas composition at the furnace exit is evaluated with mass spectroscopy. A numerical model of thermal transport phenomena developed previously is adapted to match the physical system investigated in the present study. The model is used to elucidate effects of reacting medium characteristics on particle temperature and reaction extent. Experimental and numerical results show that (1) an increase in particle size results in a decrease in carbonation extent, and (2) the carbonation step consists of fast and slow reaction regimes. The reaction rates in the fast and slow carbonation regimes increase with increasing carbon dioxide concentration. The effect of carbon dioxide concentration and the distinction between the fast and slow regimes become more pronounced with increasing particle size.